TY - JOUR
T1 - Visualization and topography of the stray magnetic field of crack-type discontinuities in magnetic materials
AU - Ivanov, V.
AU - Bashkinova, V. N.
PY - 2006
Y1 - 2006
N2 - Configurations of the domain structure of gadolinium-cobalt amorphous films placed in spatially nonuniform magnetic fields, which are produced by cracks in steel plates, are determined. The possibility of visualization and topography of the stray fields (their normal H z component) of cracks with openings 1.5 to 50 µm wide by the use of an applied magnetic field is shown. Strip domains, which determine the coordinates of edges of cracks with an opening width d > 20 µm (or peaks in the coordinate dependences), are formed near the saturation state under the action of the field. This result is in agreement with calculated theoretical topograms. An unusual discrepancy in the positions of peaks in experimental and theoretical topograms is observed for narrow cracks (d < 10 µm). It is likely that the observed discrepancy in the position of peaks in topograms of narrow cracks is related to the interaction of crack edges during their convergence, i.e., their partial mutual magnetization reversal.
AB - Configurations of the domain structure of gadolinium-cobalt amorphous films placed in spatially nonuniform magnetic fields, which are produced by cracks in steel plates, are determined. The possibility of visualization and topography of the stray fields (their normal H z component) of cracks with openings 1.5 to 50 µm wide by the use of an applied magnetic field is shown. Strip domains, which determine the coordinates of edges of cracks with an opening width d > 20 µm (or peaks in the coordinate dependences), are formed near the saturation state under the action of the field. This result is in agreement with calculated theoretical topograms. An unusual discrepancy in the positions of peaks in experimental and theoretical topograms is observed for narrow cracks (d < 10 µm). It is likely that the observed discrepancy in the position of peaks in topograms of narrow cracks is related to the interaction of crack edges during their convergence, i.e., their partial mutual magnetization reversal.
UR - https://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcAuth=tsmetrics&SrcApp=tsm_test&DestApp=WOS_CPL&DestLinkType=FullRecord&KeyUT=000237230400002
UR - http://www.scopus.com/inward/record.url?partnerID=8YFLogxK&scp=33646405209
U2 - 10.1134/S1061830906010025
DO - 10.1134/S1061830906010025
M3 - Article
VL - 42
SP - 12
EP - 18
JO - Russian Journal of Nondestructive Testing
JF - Russian Journal of Nondestructive Testing
SN - 1061-8309
IS - 1
ER -