TY - JOUR
T1 - Influence of melt temperature treatment on the structure and phase composition of leaded brass
AU - Mysik, R. K.
AU - Svinin, V. I.
AU - Vajs, I. A.
AU - Brusnitsin, S. V.
AU - Baryshev, E. E.
AU - Kostina, T. K.
PY - 1996
Y1 - 1996
N2 - Kinematic viscosity is structure-sensitive characteristic of melt. The polytherms of kinematic viscosity are plotted for LS59-1 brass at different temperature conditions. An availability of polytherm hysteresis under heating and cooling the melt testifies the nonreversible structural changes. Metallographic analysis shows a presence of α-, β-, and Pb-phases. The rise of zinc content from 36 to 39% results in the microhardness increase due to zinc redistribution and raised saturation of α-phase with Zn.
AB - Kinematic viscosity is structure-sensitive characteristic of melt. The polytherms of kinematic viscosity are plotted for LS59-1 brass at different temperature conditions. An availability of polytherm hysteresis under heating and cooling the melt testifies the nonreversible structural changes. Metallographic analysis shows a presence of α-, β-, and Pb-phases. The rise of zinc content from 36 to 39% results in the microhardness increase due to zinc redistribution and raised saturation of α-phase with Zn.
UR - http://www.scopus.com/inward/record.url?partnerID=8YFLogxK&scp=16744363952
M3 - Статья
SP - 23
JO - Litejnoe Proizvodstvo
JF - Litejnoe Proizvodstvo
SN - 0024-449X
IS - 10
ER -