TY - JOUR
T1 - High field magnetization of metal hydrides under hydrogen pressure
AU - Ishikawa, F.
AU - Yamamoto, I.
AU - Yamaguchi, M.
AU - Bartashevich, M. I.
AU - Goto, T.
PY - 1997/5/1
Y1 - 1997/5/1
N2 - The magnetization of the metal hydrides GdFe3Hx (x=0∼3.6) and Dy6Fe23Hx (x=0∼20.3) was measured in magnetic fields up to 29 T at 77 K. For these measurements the hydrides were prepared in situ in a glass holder with gradually varying hydride composition x at room temperature. For each system the magnetization curve varied systematically with hydrogen content. The dependence of magnetization on hydrogen content is discussed.
AB - The magnetization of the metal hydrides GdFe3Hx (x=0∼3.6) and Dy6Fe23Hx (x=0∼20.3) was measured in magnetic fields up to 29 T at 77 K. For these measurements the hydrides were prepared in situ in a glass holder with gradually varying hydride composition x at room temperature. For each system the magnetization curve varied systematically with hydrogen content. The dependence of magnetization on hydrogen content is discussed.
UR - http://www.scopus.com/inward/record.url?partnerID=8YFLogxK&scp=17344375853
U2 - 10.1016/S0925-8388(96)03092-7
DO - 10.1016/S0925-8388(96)03092-7
M3 - Article
VL - 253-254
SP - 350
EP - 352
JO - Journal of Alloys and Compounds
JF - Journal of Alloys and Compounds
SN - 0925-8388
ER -
ID: 55013765