The influence of processes that occur upon large degrees of drawing deformation on magnetic and mechanical properties of patented steels with 0.24 and 0.7% C is studied. Correlational relationships between magnetic and mechanical characteristics are established. The magnitude of magnetic characteristics is shown to allow evaluation of strength and plastic properties, as well as of the extent of damage to wires being deformed.