Triple hysteresis loops were observed for amorphous ferrimagnetic Gd-Co films near the magnetic compensation temperature, which can be a consequence of both the spin-flop transition and the chemical composition gradient. In the work, an assessment of the possible chemical inhomogeneity of the films based on magnetic measurements was carried out and its relationship with the thickness of the samples was observed.